Ripoxy S-510EX is a resin with excellent fire resistance and chemical resistance for use in chemical equipment manufacturing and other fields.

1. characterization::

   • Excellent flame retardancy: Excellent flame retardant properties.
   • Excellent chemical resistance: Good resistance to chemicals.
   • Meets the requirements of ASTM E-84 Class 1: Excellent fire resistance.

2. dominance::

   • low viscosity: The resin has a low viscosity and is easy to use and process.

3. Application Areas::

   • Chemical industry: Manufacture of chemical tanks, piping, absorbers, ducts and other chemical equipment.

4. Liquid Resin Properties::

   • exterior condition: Clear and transparent.
   • stickiness: 3.0 - 5.0 dPa?s at 25℃.
   • Gel time: Curing time between 20.0 - 40.0 minutes.

5. Curing Resin Properties::

   • Casting - Performance after curing::

     • bending strength: 105 MPa (standard test ASTM D790).
     • bending modulus: 3.6 GPa (standardized test ASTM D790).
     • tensile strength: 45 MPa (standard test ASTM D638).
     • Tensile elongation: 1.5% (standard test ASTM D638).
     • heat distortion temperature: 135°C (standard test ASTM D648).
     • Barco Hardness: 42 (standard test ASTM D2583).
     • Glass transition temperature (Tg): 140°C (TMA method).
     • oxygen index:: 35%.

6. caveat::

   • Safety Precautions: Contains styrene, ensure good ventilation and wear appropriate protective equipment.
   • Storage and Handling Precautions: The resin is a UN Class 3 flammable liquid, keep away from heat or flame.
   • Precautions for use: When using curing agent and accelerator, stir the accelerator before adding curing agent.
   • Disposal Precautions: Dispose of the resin after it has been completely used up and the remaining resin needs to be cured in a water bath.