Product Description: Product Name: EHPC-60-ENF2 Chemical Composition: 1,1-Di(2-ethylhexyl)peroxydicarbonate Form: White (non-freezing) emulsion Usage: Used as free radical initiator for monomer polymerization, mainly for the polymerization of vinyl chloride (VCM). Technical data: Appearance: white emulsion Inhibitor: water/methanol Content: approx. 60% w/w Active Oxygen (AO): approx. 2.77% w/w Density (20°C): approx. 0.98 g/cm3 Viscosity (20°C): approx. 200 mPa-s Flash point: 31°C Critical temperature (SADT): approx. 0°C Cold

Product Description: ACH-80-AL3 is a colorless flowable liquid containing approximately 80% w/w of 1,1-tert-butyl cyclohexyl peroxide desensitized by alkane hydrocarbons. This cyclohexyl peroxide is used as a cure initiator (free radical source) for unsaturated polyester resins. Main application areas: Thermal compression molding of SMC or BMC in the temperature range 130 - 150°C (266 - 302°F). Technical Data: Appearance: Colorless Liquid Desensitizer: Alkyl Hydrocarbon Content: approx. 80% w/w Active Oxygen (AO) Content: approx. 8.8% w/w Density (20°C)

Product Description: NOROX? 510-80-AL3 is a colorless flowable liquid containing approximately 80% w/w of 1,1-tert-butyl cyclohexyl peroxide desensitized to alkane hydrocarbons. This cyclohexyl peroxide is used as a cure initiator (free radical source) for unsaturated polyester resins. Main application areas: Thermal compression molding of SMC or BMC in the temperature range 130 - 150°C (266 - 302°F). Technical Data: Appearance: Colorless Liquid Desensitizer: Alkane Hydrocarbons Content: approx. 801 TP3T w/w Active Oxygen (AO) Content: approx. 8.81 TP3T w/w

Product Description: BCHPC is a white, free-flowing powder composed primarily of technically pure tert-butyl cyclohexyl peroxydicarbonate. This cycloaliphatic cyclohexyl peroxydicarbonate is used as an initiator for curing unsaturated polyester resins. Technical Data: Appearance: White, free-flowing powder Peroxide content: approx. 95.01 TP3T w/w Reactive oxygen content: approx. 3.811 TP3T w/w No desensitizer Stacking density: approx. 0.50 kg/l Melting point: approx. 82°C Critical temperature (SADT): approx. 45°C "Start-up" temperature: 50°C Recommended storage temperature: below 20°C Maximum transport temperature

Product Description: NOROX? 600-CL2 is a white, free-flowing powder mixture of technically pure tert-butyl cyclohexyl peroxy dicarbonate for use as an initiator in curing unsaturated polyester resins. Technical Data: Appearance: White, free-flowing powder Peroxide content: approx. 89.01 TP3T w/w Reactive oxygen content: approx. 3.551 TP3T w/w Stacking density: approx. 0.50 kg/l Melting point: 50°C Recommended storage temperature: less than 20°C Max.

Product Information: Name: NOROX? FC-100 Ingredients: Ethyl ketone acetone peroxide + tert.Butylperoxybenzoate CAS No.: 13784-51-5 + 614-45-9 Appearance: colorless liquid Density (20 ℃): about 1.1 g/cm3 reactive oxygen content: about 4.5% w/w Flash Point: about 65 ℃ Main Uses: Used as unsaturated polyester resin curing agent. Used as a curing agent for unsaturated polyester resins, usually in combination with a cobalt catalyst at room temperature. Suitable for curing thin-walled molded parts. Characteristics and Applications: NOROX? FC-100 consists of acetone acetone peroxide and tert.Butylperoxybenzoate cured by

Product Information: Product Name: NOROX? PD-40 Chemical Composition: Acetylacetone Peroxide Appearance: Colorless Liquid Main Applications: As a curing agent for unsaturated polyester resins, mainly used for curing thin-walled molded parts with cobalt accelerators at room temperature. Technical data: Effective oxygen content: approx. 4.11 TP6T (mass fraction) Density (20°C): approx. 1.1 g/cm3 Viscosity (20°C): approx. 37 mPa-s Solubility: miscible with alcohols and phthalates Critical Temperature (SADT): approx. 60°C Storage Stability: can be stored at temperatures ranging from 10°C to 25°C and is valid for 6 months after delivery of goods. Should

Product Description: NOROX? PD-40 FRED is a red liquid containing acetylacetone peroxide with reduced sensitivity by means of an acetone diol coolant. The peroxide is suitable for use as a free radical initiator for curing unsaturated polyester resins. Main application: In combination with a cobalt catalyst for curing thin-walled molded parts at room temperature. Technical Data: Appearance: Red Liquid Sensitivity Degraders: Glycol, Acetone Diol Active Oxygen (AO): Approx. 4.1% w/w Density (20°C): Approx. 1.1 g/cm3 Viscosity (20°C): Approx. 37 mPa-sec Miscible with alcohols, phthalates

DESCRIPTION: NOROX WPC-100 is a liquid based on a peroxide formulation of acetylacetone peroxide and tert-butyl peroxybenzoate. It is emulsified.NOROX WPC-100 has been developed to meet the regulations for drinking water applications. Technical Data: Appearance: Liquid Active Oxygen Content: 3.7% - 4.1% Flash Point (Seta C.C.): > 65°C Density (20°C): 1.07 - 1.11 g/cm3 Viscosity (20°C): 80 - 90 mPas Solubility: Soluble in a variety of organic solvents, e.g. ethers,